Mo in CA6NM martensitic stainless steel

Mo – the addition of alloying element Mo in CA6NM martensitic stainless steel is beneficial to the strength. And also to toughness and corrosion resistance. Mo is a ferrite forming element. It can reduce the Ms temperature.

Navigation Table

The role of Mo in CA6NM martensitic stainless steel

Mo——the addition of alloying element Mo in martensitic stainless steel is beneficial to the strength. And also to toughness and corrosion resistance. Mo is a ferrite forming element. It can reduce the Ms temperature. The addition of Mo in super martensitic steel can reduce the martensite unidirectional zone. Meanwhile, Mo can promote the passivation of Cr in some reducing corrosive media. Thus, Mo can improve the corrosion resistance of Cr-Ni stainless steel in reducing acid. And inhibit the pitting corrosion of Cl- and improve the intergranular corrosion resistance of steel.

Mo is a kind of austenite stabilization element, like Ni. Excessive addition can lead to the formation of retained austenite. In martensitic stainless steel, Mo content is generally controlled below 5%.

CA6NM ASTM A743
CA6NM ASTM A743

CA6NM Chemical Composition

CA6NM-chemical-composition

CA6NM Martensitic Stainless Steel

CA6NM-mechanical-property

Application of alloys in CA6NM martensitic stainless steel